E71T-1 1.0/1.2/1.4/1.6mm Flux Cored MIG Welding Wire
Flux Cored Arc Welding Wire (FCAW) AWS A5.20 E71T-1, is used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery etc.
Our advantages is stable arc, little spatter, less smoke; higher deposition efficiency; excellent welding performance; easy restrike.
Confirm to standard:
AWS A5.20 E71T-1,
E501t-1
Chemical Composition(%)(Shielding Gas:CO2)
| Chemical Composition |
C |
Mn |
Si |
S |
P |
| Guarantee Value |
≤0.18 |
≤1.75 |
≤0.90 |
≤0.030 |
≤0.030 |
| General Result |
0.05 |
1.36 |
0.41 |
0.008 |
0.012 |
Mechanical Properties of Deposited Metal(Shielding Gas:CO2)
| Test Item |
Rm(MPa) |
ReL/Rp0.2(MPa) |
A(%) |
KV2(J) |
| -20℃ |
| Guarantee Value |
≥480 |
≥400 |
≥22 |
≥27 |
| General Result |
560 |
480 |
28 |
145 |
Diffusion hydrogen content of the deposited metal (Mercury Method):≤10ml/100g
X-Ray Radiographic Test Requirements:Grade II
Reference Current(DC+)
| Size(mm) |
Φ1.0 |
Φ1.2 |
Φ1.4 |
Φ1.6 |
| Current Range (A) |
Flat Position |
120~250 |
120~300 |
150~400 |
180~450 |
| Vertical Upward welding/ Overhead position |
120~210 |
120~260 |
150~270 |
180~280 |
| Vertical Downward weldingOverhead position |
200~250 |
200~300 |
220~300 |
250~300 |
| Horizontal Welding |
120~230 |
120~280 |
150~320 |
180~350 |
Notes:
1.Adopt degreasing and rust cleaning process before operate.
2.Shielding gas flow: 20-25L/min when welding
3.Extension: 15-25mm
4.The humidity of welding wire storage should be less than 60%
5.Storage period: Vacuum packaging less than 1 Year, other packaging less than half year.